钱桂安洪友士
金属学报
选用40Cr结构钢, 分别在空气、水和3.5%NaCl水溶液中进行旋转弯曲疲劳实验, 研究环境介质对该结构钢高周和超高周疲劳特性的影响. 结果表明, 40Cr钢在水环境中的疲劳强度比在空气中明显降低; 在3.5%NaCl水溶液环境中的疲劳强度比在水中低. 断面观察显示, 在水和3.5%NaCl水溶液中, 疲劳裂纹多源萌生; 在稳态扩展阶段, 裂纹沿晶界扩展并存在广泛分布的沿晶二次裂纹. 。
关键词:
40Cr结构钢
,
very-high-cycle fatigue
,
environmental media
,
fatigue strength
,
fatigue crack initiation
陈文哲
,
钱匡武
金属学报
本文着重研究了动态应变时效(DSA)预处理对18-8型奥氏体不锈钢室温纯弯疲劳强度的影响。结果表明,DSA预处理显著提高材料纯弯疲劳强度,其强化效果随预应变温度和预应变量的增加而提高,其疲劳极限比固溶态提高87％,比相应的冷变形态提高20％。金属薄膜电镜观察结果表明,材料经DSA预处理后,形成了均匀、高密度、稳定的位错网络结构。在随后的疲劳过程中,它们有效地抑制了疲劳裂纹的萌生和扩展。
关键词:
动态应变时效
,
austenitic stainless steel
,
fatigue strength
M.Szubryt
,
J.Brózda
金属学报(英文版)
The influence of welding parameters of butt joints, made by three processes (MMA, MAGand T.I.M.E), on their geometric characteristics has been evaluated, which in turn caused a change of the fatigue strength. That fore the statistic analysis and FEM were used and a method developed in the Institute of Welding, which consist in a direct connection of parameters used during welding with the fatigue strength of joints welded by various processes. It has been proven, among others.which by using more advanced welding processes (TLM.E) the fatigue strength of welded joints can be increased in comparison to joints welded by MMA and MAG.
关键词:
fatigue strength
,
null
,
null
刘安民
,
钱书琨
,
汪新衡
,
朱航生
材料导报
对60Si2Mn弹簧钢进行了优化余热淬火:920℃加热奥氏体化,保温20 min,随后冷至860℃出炉进行油淬,400℃回火1.5h,空冷.再对60Si2Mn弹簧钢进行了强力喷丸及低温时效处理.结果表明,60Si2Mn弹簧钢经此复合优化处理工艺后残余压应力松弛平缓,其屈强比和疲劳强度显著提高,综合力学性能也得到明显改善,完全能满足汽车板弹簧使用要求.
关键词:
60Si2Mn弹簧钢
,
余热淬火
,
强力喷丸
,
低温时效
,
残余压应力
,
屈强比
,
疲劳强度
张杰
,
闫志峰
,
王文先
,
王志斌
,
王凯
,
张红霞
,
张心保
材料工程
doi:10.11868/j.issn.1001-4381.2015.02.013
采用红外热像法研究了443铁素体不锈钢在疲劳试验过程中表面温度场的变化规律,提出了采用△T-Nf曲线预测疲劳寿命的方法.结果表明:温升极限值△T=3.18℃,即当△T＞3.18℃时,试样发生疲劳断裂,与实测温升值3.49℃相比,误差为8.89％.利用△T-Nf曲线预测443铁素体不锈钢在5×106循环次数下的疲劳强度为277.97MPa,与传统方法测得结果284.45MPa相对误差为2.28％.
关键词:
443铁素体不锈钢
,
温度场
,
疲劳强度
,
红外热像法